China Ningbo Tongchuang Strong Magnet Material CO.LTD. is a high-tech company specializing in NdFeB magnet and magnetic materials, digital fluxmeter manufacturer, researching, developing and applications. We also are manufacturing and marketing other custom digital fluxmeters permanent magnets, such as Sm-Co, Al-Ni-Co, hard ferrites and rubber magnets. ISO 9000 QC systems is through our all production processes, with the assistance of advanced testing and inspection equipments and techniques. We also take RoHS requirement as the guideline in material selection. Tongchuan magnets have been used widely in small motors, instruments, electronic devices, auto parts, MRIs, Speakers and a great variety of other applications. |
 |
Use coating thickness Analysis tester to inspect the thickness of coating by electroanalysis.
Or Perform material coating thickness analysis using anode dissolve coulometry. |
Coating Thickness Meter |
|
 |
Test condition :
Temperature:35C Degree,5% NaCl ,Continous spray,example.Nickel coating ,spray for 24 hours.
Test Standard/Criterion:
Coating is good ,doesn't get off,no bubbles,no dots.no rust appear. |
| Salt Spray Test(SST) |
|
 |
Our PCT And HAST TEST are all finished in their inspection instruments
One test is Pressure cooker Test (PCT):
-PCT TEST is used to test the magnets with Coating.
Test condition :
121C and 95% RH and 2 atmos pressure, test for 24 hours,example.Nickel coating
Test Standard/Criterion:
Coating does not Get off, there are no air bubbles or dots Appear
The second test is Highly Accelerated Stress Test (HAST
HAST TEST is used to test the un-coated magnets,to check the weight loss of magnets at the following test condition.
Test Condition:
132C and 95%-100% RH and 3 Atmos Pressure,Test for 7 Days.
The following is some weight loss datas of our magnets,which we tested for other customers in the past |
|
| HAST(Highly Accelerated Stress Test) Results |
| Grade |
Dimension |
Test Condition |
Weight Before Test(mg) |
Weight After Test(mg) |
Weight Loss (mg/cm2) |
| Pressure(Mpa) |
Temperature(℃) |
Time (Hour) |
| 38SHT |
10*10*9 |
0.2 |
121 |
120 |
6820.1 |
6809.6 |
1.88 |
| |
|
|
|
|
6818.2 |
6805.5 |
2.27 |
| |
|
|
|
|
6818.8 |
6806.3 |
2.23 |
| |
|
|
|
|
6785.7 |
6770.5 |
2.71 |
| |
|
|
|
|
6784.5 |
6768.4 |
2.88 |
| Average Weight Loss |
|
|
|
|
|
2.39 |
| 33UHT |
D25.4*2.54 |
0.2 |
121 |
168 |
9708.7 |
9693.2 |
1.28 |
| |
|
|
|
|
9717.9 |
9701.7 |
1.33 |
| |
|
|
|
|
9701.6 |
9689.0 |
1.04 |
| |
|
|
|
|
9703.5 |
9689.3 |
1.17 |
| |
|
|
|
|
9663.2 |
9648.3 |
1.23 |
| |
|
|
|
|
9693.2 |
9678.9 |
1.18 |
| |
|
|
|
|
9613.3 |
9600.2 |
1.08 |
| |
|
|
|
|
9701.5 |
9686.9 |
1.20 |
| |
|
|
|
|
9712.9 |
9699.2 |
1.13 |
| |
|
|
|
|
9687.8 |
9671.2 |
1.37 |
| |
|
|
|
|
9700.4 |
9674.5 |
2.13 |
| Average Weight Loss |
|
|
|
|
|
1.28 |
| N45 |
10*10*5 |
0.2 |
121 |
120 |
3777.6 |
3774.4 |
0.80 |
| |
|
|
|
|
3788.7 |
3783.6 |
1.27 |
| |
|
|
|
|
3792.0 |
3785.6 |
1.60 |
| |
|
|
|
|
3788.9 |
3782.9 |
1.50 |
| |
|
|
|
|
3774.4 |
3770.1 |
1.08 |
| Average Weight Loss |
|
|
|
|
|
1.25 |
| L-30AHT |
10*10*5 |
0.2 |
121 |
120 |
3849.6 |
3844.6 |
1.25 |
| |
|
|
|
|
3855.7 |
3850.2 |
1.38 |
| |
|
|
|
|
3873.7 |
3870.3 |
0.85 |
| |
|
|
|
|
3869.3 |
3864.1 |
1.30 |
| |
|
|
|
|
3860.4 |
3855.6 |
1.20 |
| Average Weight Loss |
|
|
|
|
|
1.20 |
| 33EHT |
10*10*8 |
0.2 |
121 |
144 |
6155.6 |
6148.8 |
1.31 |
| |
|
|
|
|
6125.9 |
6120.1 |
1.12 |
| |
|
|
|
|
6131.3 |
6125.5 |
1.12 |
| |
|
|
|
|
6053.0 |
6047.1 |
1.13 |
| |
|
|
|
|
6127.7 |
6120.5 |
1.38 |
| Average Weight Loss |
|
|
|
|
|
1.21 |
| 42HT |
10*10*6 |
0.2 |
121 |
144 |
4525.8 |
4520.5 |
1.20 |
| |
|
|
|
|
4554.1 |
4547.6 |
1.48 |
| |
|
|
|
|
4532.4 |
4527.7 |
1.07 |
| |
|
|
|
|
4569.5 |
4559.6 |
2.25 |
| |
|
|
|
|
4523.9 |
4517.1 |
1.55 |
| Average Weight Loss |
|
|
|
|
|
1.51 |
| L-38SHT |
R29.5*R29.5*20*15.7*2 |
0.25 |
126 |
168 |
4307.0 |
4284.2 |
3.03 |
| |
|
|
|
|
4305.0 |
4281.6 |
3.11 |
| Average Weight Loss |
|
|
|
|
|
3.07 |
| L-38SHT |
R29.5*R29.5*23.5*24*3 |
0.25 |
126 |
168 |
11898.5 |
11823.9 |
5.37 |
| |
|
|
|
|
11805.0 |
11749.3 |
4.01 |
| |
|
|
|
|
11901.0 |
11834.3 |
4.80 |
| |
|
|
|
|
11899.0 |
11866.9 |
2.31 |
| |
|
|
|
|
11885.9 |
11822.7 |
4.55 |
| Average Weight Loss |
|
|
|
|
|
4.21 |
| L-38SHT |
R231.5*r223.5*75.5*16.52 |
0.2 |
121 |
96 |
307090.0 |
306988.2 |
0.88 |
| Average Weight Loss |
|
|
|
|
|
0.88 |
| L-38SHT |
R229.8*r223.8*17°*83 |
0.2 |
121 |
96 |
256240.0 |
256121.9 |
0.91 |
| Average Weight Loss |
|
|
|
|
|
0.91 |
| 33EHT |
R98.5*R93.5*39*50 |
0.2 |
121 |
120 |
47099.9 |
46954.3 |
3.12 |
| Average Weight Loss |
|
|
|
|
|
3.12 |
| 33EHT |
10*10*10 |
0.2 |
121 |
120 |
7691.2 |
7673.1 |
3.02 |
| Average Weight Loss |
|
|
|
|
|
3.02 |
| 38UHT |
13.72*7.37*2.67 |
0.25 |
126 |
96 |
206.48 |
202.79 |
1.17 |
| |
|
|
|
|
205.64 |
202.3 |
1.06 |
| |
|
|
|
|
206.46 |
202.99 |
1.10 |
| |
|
|
|
|
205.99 |
191.02 |
4.75 |
| Average Weight Loss |
|
|
|
|
|
2.02 |
| L-33EHT |
R98.5*R93.5*39*50 |
0.2 |
121 |
120 |
47099.9 |
47055.9 |
1.06 |
| Average Weight Loss |
|
|
|
|
|
1.06 |
| 38HT |
57*32*12 |
0.2 |
121 |
96 |
157530.0 |
157361.1 |
2.92 |
| Average Weight Loss |
|
|
|
|
|
2.92 |
| L-33EHT |
15*9*3 |
0.2 |
121 |
120 |
3170.7 |
3166.5 |
1.01 |
| |
|
|
|
|
3172.5 |
3168.2 |
1.04 |
| Average Weight Loss |
|
|
|
|
|
1.03 |
|
|
|
| Contact us |
Ningbo Tongchuang Strong Magnet Material Co., Ltd
Add: NO.318.Kexin Road, Wang Chun Industrial Area, Yinzhou, Ningbo, Zhejiang, China
TEL: 86-574- 88170908, 88089786
Fax: 86-574- 88170906, 88089789
E-mail: sales@ndmagnets.com (General Inquiry) |
|
|